1.1This practice covers procedures for eddy current examination of hot ferromagnetic bars above the Curie temperature where the product is essentially nonmagnetic, but below 2100 °F (1149 °C).

1.2This practice is intended for use on bar products having diameters of ¹/₂in. (12.7 mm) to 8 in. (203 mm) at linear throughput speeds up to 1200 ft/min (366 m/min). Larger or smaller diameters may be examined by agreement between the using parties.

1.3The purpose of this practice is to provide a procedure for in-line eddy current examination of bars during processing for the detection of major or gross surface discontinuities.

1.3.1The types of discontinuities capable of being detected are commonly referred to as: slivers, laps, seams, roll-ins (scale, dross, and so forth), and mechanical damage such as scratches, scores, or indentations.

1.4This practice does not establish acceptance criteria. They must be specified by agreement between the using parties.

1.5The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.6This practice does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this practice to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.